1060 Aluminum Coil and Strip Chemical Composition:
Iron (Fe) 0.35 Manganese Mn: 0.03
Magnesium (Mg) 0.03 Silicon (Si) 0.25
Zinc (Zn) 0.05 Titanium (Ti) 0.03
Copper (Cu) 0.05, aluminum (Al) 99.6 or above
Mechanical properties:
Tensile strength σ b (MPa) ≥ 75
Conditional yield strength σ 0.2 (MPa) ≥ 35
Main features and application scope:
1060 aluminum coil is formed by adding a small amount of copper element to pure aluminum, which has excellent forming processing characteristics, high corrosion resistance, good weldability and conductivity. 1060 aluminum coil is widely used in products that do not require high strength, such as chemical instruments, thin plate processing parts, deep drawn or spun concave vessels, welded parts, heat exchangers, clock surfaces and dials, nameplates, kitchenware, decorations, reflective instruments, etc.
Heat treatment range:
Rapid annealing: heating temperature 350-410 ℃; The insulation time varies between 30 and 120 minutes depending on the effective thickness of the material; Air or water cooling. High temperature annealing: heating temperature 350-500 ℃; When the thickness of the finished product is ≥ 6mm, the insulation time is 10-30min, and when it is<6mm, it should be fully penetrated; Air cold. Low temperature annealing: heating temperature of 150-250 ℃; The insulation time is 2-3 hours; Air or water cooling.